밀도 높은 질화붕소 형상
DENSE BORON NITRIDE SHAPE
DENSE BORON NITRIDE SHAPE
Dense boron nitride shapes are produced either by hot pressing(grade CDBN, SOBN, SCBN, OBN) or hot isostatic pressing (grade HDBN)
Properties
- Excellent machinability(conventional metal working tools can be used)
- Outstanding temperature shock resistance
- Excellent electrical insulation - even at high temperature
- Resistant to molten metals and glass
- In addition, it has excellent high temperature lubrication and excellent machining with lightweight materials.
Applications
Grade |
Application |
HDBN |
Electrical insulators for high temperature applications |
CDBN |
Spanker plates used in the production of TV tubes |
SOBN |
Breakrings for the horizontal continuous casting of high-alloy steels |
SCBN |
Breakrings for low-alloy steels |
OBN 1 |
Casting nozzles and other components for the aluminium industry |
OBN 2 |
Nozzles for casting nickel and cobalt-based alloys |
※ 위 표는 일부품목만을 보여주고 있습니다. 이외의 품목에 관하여 문의 사항이 있으시면 연락 주십시오.
physical property table
B/N 이형제
BN SUSPENSION
DENKA Boron Nitride 코팅제
코트U, 코트S두가지 품종이 있으며 내식성, 내열성, 윤활성, 이형성을 부여한다.
BN 코팅의 용도
- 내열, 내식도료 : 용융물에 대한 침식방지 효과
- 윤활, 이형제 : 각종 금속 및 유리등의 거푸집등에 사용되며 침식방지, 이형, 산화방지효과
- 고온용결합제 : 성형체의 접착, 각종 내화물의 고온용 결합체
코팅제의 품종 및 사용법
| 품종 | 적용 | 도포법 | 희석재 | 연소온도 | 사용온도 |
| 코트 U | 스텐레스 , 주철, 비철금속, 흑연, 각종 내화물 |
스프레이 침지 쇄모칠 |
방향족 탄화수소 |
180~200도 (3시간) 400~500도 (30분) |
산화분위기 900도 |
| 코트 S | 유리, 스텐레스, 비철금속, 석영 | 물 | 200~900도 (15분, 최저 200도) | 산화분위기 900도 비산화 분위기 1500도 |
사용시 주의사항
- 1. 유기용제가 포함되어 있어 환기를 충분히 시켜주십시오
- 2. 도포후 굽기전에 상온건조를 행하여 주십시오
- 3. 도막의 두께는 0.05mm가 적당합니다
BN Spray
윤활 이형제로서 스프레이 형태로 작업능률이 향상된다.
용도 : 문드러짐의 방지 및 조립정도 향상. 이상마찰 방지
- 고온윤활성 : 고온에서 용융금속, 용융유리등의 윤활 이형제로 사용
- 섬유, 식품제조기계관계에 오염방지 및 청결유지
- 프레스 작업시 금형의 이형
- 고온용융체의 이형(공기중 900℃, 진공하에서 2000℃까지)
스프레이의 종류
- 드라이타입으로 용량은 250g
사용시 주의사항
- 1. 유기용제가 포함되어 있어 환기를 충분히 시켜주십시오
- 2. 도포후 굽기전에 상온건조를 행하여 주십시오
- 3. 도막의 두께는 0.05mm가 적당합니다